Grade
|
|
Apparent
Pororsity % |
Hardness
On Shore "D" Scale |
Compressive
Strength N / mm2 |
Transverse
Strength N / mm2 |
Shear
Strength N / mm2 |
Tensile
Strength N / mm2 |
Heat
Resistance 0c |
Impregnation
|
|
IC-1101
|
1.71
|
1
|
98
|
195
|
64
|
41
|
59
|
200
|
Resin
|
|
IC-1102
|
1.70
|
1
|
95
|
190
|
59
|
42
|
56
|
200
|
Resin
|
|
IC-2101
|
1.78
|
1
|
98
|
200
|
66
|
41
|
60
|
200
|
Resin
|
|
IC-2102
|
1.75
|
1.5
|
92
|
185
|
57
|
40
|
55
|
350
|
High
Temp Resin
|
|
IC-3102
|
1.74
|
1
|
95
|
180
|
55
|
36
|
54
|
210
|
Alkali
Proof Resin
|
|
IC-4101
|
2.60
|
1
|
98
|
195
|
62
|
43
|
58
|
200
|
Lead
|
|
IC-4102
|
2.40
|
1
|
99
|
205
|
67
|
44
|
61
|
350
|
Copper
& Lead
|
|
IC-4103
|
4.10
|
1
|
99
|
215
|
68
|
45
|
64
|
200
|
Copper
Lead & Tin
|
|
IC-5101
|
1.70
|
1
|
92
|
165
|
49
|
34
|
48
|
350
|
High
Temp. Modified Resin
|
|
IC-6001
|
1.71
|
1
|
90
|
160
|
48
|
34
|
47
|
200
|
Resin
|
|
IC-6002
|
1.69
to 1.71
|
16
to 18
|
70
|
42
|
23
|
18
|
15
|
600o
in Oxidixing
2500o in Non-Oxidising |
Pure
Graphite
|
|
IC-6003
|
1.78
to 1.80
|
6
to 8
|
80
|
47
|
26
|
21
|
17
|
600o
in Oxidixing
2500o in Non-Oxidising |
Pure
Graphite
|
|
Note
: The figures given in the above table are of average values based on
the data obtained from test Specimens. The information is presented in
good faith and does not constitute a part of our terms and conditions
of sale unless so specified.
|
|
||||